Study on Composition and Mechanical Property of New High Abrasion Resistant Alloy Used in High Arc Spaying

Spraying wire was widely used in remanufacturing work piece for worn failure. With the demand of high abrasion resistant wire, new type alloy was developed. The solidification structures of the new high abrasion resistant alloy (HARA) containing Mn, Cr, Si, C and the structure was studied after tension by scanning electron microscopy (SEM). The phase evolution was analyzed by X-ray diffraction and Rockwell hardness evaluated on the hardness testing. The abrasion behavior of HARA alloy used in the liner of wet-grinding machine in metallurgical industry is investigated under impacted energy of 0.5-3 J in acid-ironstone slurry; the test was carried out by a modified MLD-10 tester. The result show that the solidification structures of HARA alloy consist of austenitic Fe and the hardness neared to HRC60. Under the high energy, the wear resistance of HARA alloy is three times more than Mn13. Therefore, the new material has better abrasive wear resistance and lower environmental impact