Spintronic terahertz emission from Ni/Pt bilayer grown on MgO

Spintronic THz emission from Ni/Pt bilayer grown on MgO is reported based on the novel THz emitter using metallic structures. The Ni metal was deposited first on a MgO substrate and capped with a thin Pt metal via electron beam deposition. The THz emission data was obtained using a standard terahertz time-domain spectroscopy setup using a Ti: sapphire laser excitation source. Initial measurements were done using 800nm excitation with 7 mW and 185 mW pump powers under upward and downward magnetic field orientations. Polarity reversal of the terahertz signal was observed upon changing the orientation of the magnetic field. Maximum amplitude was found at 0.5 THz with bandwidth up to ~6 THz. A saturation fluence of 85.04 mJ/cm2 was calculated from the pump fluence-dependence plot of the THz peak-to-peak signal. The results are consistent with the spintronic THz emission due to the inverse spin-Hall effect and provide insights for future development and optimizations.