Hybrid composites of short acetylated kenaf bast fiber and conducting polyaniline nanowires in epoxy resin

This article reports the preparation and characterization of newly developed hybrid composites consisting of epoxy resin (EP) matrix, acetylated kenaf bast fiber (AKF) and conducting polyaniline (PANI) nanowires. Initially, the EP/AKF composites were prepared by varying the AKF loading (5–30 wt%). The EP/AKF displayed an optimum tensile strength at 20 wt% AKF loading which was higher than that of untreated kenaf fiber EP composites (EP/UKF). The hybrid composites of EP/AKF/PANI were then prepared by using 20 wt% AKF loading with PANI inclusions from 2 to 14 wt%. The addition of PANI into EP/AKF induced positive electrical properties without considerably sacrificing its mechanical integrity. It was found that the electrical percolation threshold of these hybrid composites was at 11 wt% of PANI loading. PANI inclusions at above the percolation loading resulted in reduction of tensile and flexural strength. Meanwhile, no significant mechanical loss was observed below the threshold. The fracture morphological analysis revealed the occurrences of PANI nanowires pull out from the matrix. The Fourier transform infrared spectroscopy showed that the PANI component still maintained its doped condition inside the EP/20AKF. Water absorption and thermal analysis indicate that the PANI incorporation induced lower water uptakes and greater thermal stability to the EP/20AKF, respectively.