Abstract
- The deformation of four types of thin films of polyoxymethylene is discussed. Failure, even at elevated temperatures, occurred by micronecking or in a brittle manner. Slip bands were observed in some of the samples. Moire patterns from portions of the sample indicated little internal distortion of the lamellae during the brittle failure. Micronecking with fibril formation occurred primarily during draw at temperatures near the α transition temperature. The results are in general agreement with concepts of the deformation process previously developed on the basis of work with thin films of polyethylene but cannot be applied directly to the mechanism of deformation of bulk samples. Die Verformung von vier auf verschiedene Weise hergestellten Typen von dunnen Polyoxymethylenfilmen wurde untersucht. Die Filme zerresen, sogar bei erhohter Temperatur, unter mikroskopischer Schulter-Hals-Bildung oder durch sproden Bruch. In einigen Proben wurden Gleitbander beobachtet. Moire-Figuren an verschiedenen Stellen der Proben deuten auf Verzerrungen innerhalb der Lamellen wahrend des sproden Zerreisens. Schulter-Hals-Bildung verbunden mit Fibrillenbildung erfolgt besonders dann, wenn die Dehnung im Bereich der α-Ubergangs-Temperatur erfolgt. Die Ergebnisse sind in Ubereinstimmung mit Vorstellungen uber den Deformationsvorgang, die fruher an Hand von Untersuchungen mit Polyathylenfilmen entwickelt wurden; sie erlauben aber keine direkten Aussagen uber den Mechanismus der Deformation groserer Probekorper.
Details
- ISSN :
- 0025116X
- Volume :
- 118
- Database :
- OpenAIRE
- Journal :
- Die Makromolekulare Chemie
- Accession number :
- edsair.doi...........44ad9dc26558cb5477db62378d6efa0e