Development ofγ-fibre recrystallisation texture in medium–chromium ferritic stainless steels

The texture development and γ-fibre recrystallisation texture formation mechanism of ferritic stainless steels under different rolling processes were investigated. It was shown that the surface texture development was absolutely different from the centre texture development. In conventional rolled band, strong α-fibre was formed at the centre layer and it was weakened after hot band annealing; after cold rolling, the centre texture was characterised by sharp α-fibre and weak γ-fibre with a peak at {111} , and non-uniform γ-fibre recrystallisation texture was developed. By contrast, in warm rolled band, the centre texture consisted of weakened α-fibre and sharpened γ-fibre, and {111} became the prominent component after hot band annealing. The α-fibre and γ-fibre with a peak at {111} were intensified at the centre texture after cold rolling, resulting in the formation of uniform γ-fibre recrystallisation texture. It was indicated that the formation mechanism of γ-fibre recrystallisati...