Synthesis and Characterization of a Hydroxylated Dendrimeric Gene Delivery Carrier

1 H NMR. The newly synthesized polymer, PAMAM-R-PO was able to completely retard pDNA from a charge ratio of 2. The average diameter of PAMAM-R-PO polyplex was found to be 242 nm at a charge ratio of 30. The Zeta-potential value of PAMAM-R-PO polyplex was able to reach 20-30 mV over a charge ratio of 10. PAMAM-R-PO indicated higher cell viability than unmodified PAMAM-R on HeLa and 293 cells because of its hydroxylated amines. Transfection experiments on 293 cells showed that the transfection efficiency of PAMAM-R-PO was found to be 1.5-1.9 times higher than that of PEI25kDa at a charge ratio of 30. The polymer eventually displayed about 2 times greater transfection efficiency than PAMAM-R at the same charge ratio in the absence of serum. Therefore, we concluded that the modification of primary amines of PAMAMR to amino alcohols gives positive effects such as reduced cytotoxicity and enhanced transfection efficiency on 293 cells for gene delivery potency of PAMAM-R.