ChemInform Abstract: Magnetic and Charge Transport Properties of the Na-Based Os Oxide Pyrochlore

The Na-based osmium oxide pyrochlore was synthesized for the first time by an ion-exchange method using KOs{sub 2}O{sub 6} as a host. The composition was identified as Na{sub 1.4}Os{sub 2}O{sub 6}.H{sub 2}O by electron probe micro-analysis, thermogravimetric analysis, and structural analysis using synchrotron X-ray diffraction. Na{sub 1.4}Os{sub 2}O{sub 6}.H{sub 2}O crystallizes in a regular pyrochlore structure with some defects (space group: Fd-3m, a=10.16851(1) A). Electrical resistivity, heat capacity, and magnetization measurements clearly showed absence of superconductivity down to 2 K, being in large contrast to what was found for the beta-type pyrochlore superconductor AOs{sub 2}O{sub 6} (A=Cs, Rb, and K). The Sommerfeld coefficient is 22 mJ K{sup -2} mol{sup -1}, being the smallest among AOs{sub 2}O{sub 6}. A magnetic anomaly at {approx}57 K and associated magneto-resistance (+3.7% at 2 K in 70 kOe) were found. - Graphical abstract: Crystal structure of the Na-based Os oxide pyrochlore Na{sub 1.4}Os{sub 2}O{sub 6}.H{sub 2}O.