Post-Aging Retrogression in Magnesium Alloys with Two Rare-Earth Metals Belonging to Different Groups

The phenomenon of post-aging retrogression in magnesium alloys containing two rare-earth metals belonging to different groups, i.e., yttrium Y (the yttrium group) and samarium Sm (the cerium group), is investigated. It is shown that retrogression may occur in alloys with different proportions of yttrium and samarium aged at 200°C for maximum hardness and then annealed at somewhat higher temperatures (250 and 300°C). The process is possible due to decomposition of the supersaturated magnesium solid solution. The degree of the retrogression is shown to depend on the temperature and duration of the post-aging annealing and on the yttrium- to-samarium proportion in the alloys.