Impact of time-dependent annealing on TiO2 films for CMOS application

Post-deposition annealing (PDA) is the inherent part of sol-gel fabrication process to achieve the optimum device performance, especially in CMOS applications. The annealing removes the oxygen vacancies and improves the structural order of dielectric films. The process also reduces the interface related defects and improves the interfacial properties. In this work, we have integrated the sol-gel spin-coating deposited high-κ TiO2 films in MOS. The films are fired at 400°C for the duration of 20, 40, 60 and 80 min. The thicknesses of the films were found to be of ∼ 30 nm using ellipsometry. The (Al/TiO2/p-Si) devices were examined with current-voltage (I-V) and capacitance-voltage (C-V) at room temperature to understand the influence of firing time. The C-V and I-V characteristic showed a significant dependence on annealing time such as variation in dielectric constant and leakage current. The accumulation capacitance (Cox), dielectric constant (κ) and the equivalent oxide thickness (EOT) of the film fired...