Microstructure of the pulp and paper additives for stone-mastic asphalt concrete

The paper is focused on investigation of the nature and size of cellulose fibers in the structure of stabilizing additives for stone-mastic asphalt concrete, as well as on determination of fibers retention capacity based on their geometric parameters. To obtain the results a scanning electron microscope JSM-6510LV was used, with the help of which 15 to 20 photomicrographs were obtained. It was found out that in all inspected samples of stabilizing additives over 80% of pulp and paper fibers have a band structure with filaments from 0.56 to 1.4 micrometer in length. The fiber thickness in all cases slightly varies within the range of 0.008 to 0.021 micrometer. For a more detailed analysis of the additives the X-ray microanalysis was carried out. The results showed that in all cases the component distribution of the chemical elements present in the additive is inhomogeneous and has two fundamental differences in the oxygen (O) and carbon (C) content. ARMIDON additives contain more than 79% carbon (C) and just 6-13% oxygen (O). VIATOP 66 and SD-1 additives contain up to 61% carbon (C) and up to 48% oxygen (O). Tests to determine the runoff of the organic binder showed that additives with cellulose fiber filaments up to 0.6 micrometers in length hold bitumen worse than additives with cellulose fiber filaments 1.4 micrometers in length.The paper is focused on investigation of the nature and size of cellulose fibers in the structure of stabilizing additives for stone-mastic asphalt concrete, as well as on determination of fibers retention capacity based on their geometric parameters. To obtain the results a scanning electron microscope JSM-6510LV was used, with the help of which 15 to 20 photomicrographs were obtained. It was found out that in all inspected samples of stabilizing additives over 80% of pulp and paper fibers have a band structure with filaments from 0.56 to 1.4 micrometer in length. The fiber thickness in all cases slightly varies within the range of 0.008 to 0.021 micrometer. For a more detailed analysis of the additives the X-ray microanalysis was carried out. The results showed that in all cases the component distribution of the chemical elements present in the additive is inhomogeneous and has two fundamental differences in the oxygen (O) and carbon (C) content. ARMIDON additives contain more than 79% carbon (C) and ju...