On the relaxation effect due to the stress-induced diffusion of interstitial oxygen in tantalum

The diffusion coefficient of interstitial oxygen atoms in tantalum has been determined by measurements of the elastic energy dissipation as a function of the temperature. The relaxation peak related to this process was found with its maximum at 346 °C for a vibration frequency of about 20 kHz. The analysis of the experimentl data give an activation energyW=1.19 eV and a diffusion constantD 0=1.9 · 10−2 cm2/s, in very good agreement with some previous results obtained at very low frequencies. A description of the new features of the experimental technique is also given. Был определен козффициент диффуэии внутренних атомов кислорода в тантале, путем иэмерений упругой знергетической диссипации, как функции температуры. Был обнаружен релаксационный пик, свяэанный с зтим процессом, с максимумом при 346 °С для частоты колебаний около 20 kHz. Аналиэ зкспериментальных данных дает знергию активацииW=1.19 зВ и постоянную диффуэииD 0=1.9·10−2 см2/сек, что находится в очень хорощем согласии с некоторыми предыдушими реэультатами, полученными при очень ниэких частотах. Также приводится описание новых особенностей зкспериментальной техники.