Preparation and corrosion protection of polypyrrole/SiO2nanocomposite doped with 3‐nitrosalicylic acid on aluminum

Polypyrrole/SiO2nanocomposite doped with 3‐nitrosalicylic acid was synthesized in three concentrations of 3‐nitrosalicylic acid: 0.01 m, 0.005 m, and 0.0025 m. FTIR spectroscopy, thermogravimetric analysis (TGA), Raman scattering spectroscopy, and FESEM imaging further assisted in determining the shape and structure of the polypyrrole/nanocomposite product. The aluminum protection arrangement of the paint film comprising polypyrrole/SiO2nanocomposite doped with 3‐nitrosalicylic acid was proven by electrochemical methods. The salt spray test results also demonstrated the protective efficacy of the paint film comprising polypyrrole/SiO2nanocomposite doped with 3‐nitrosalicylic acid to suppress corrosion. The best corrosion prevention results were obtained with a polypyrrole/SiO2nanocomposite dispersion paint film doped with 0.01 m3‐nitrosalicylic acid at a concentration of 2%. Open circuit potential curves of aluminum coated with original paint film (Mo), paint film containing SiO2(T1), and paint film containing Ppy/SiO2(T2, T3, T4, and T5) according to immersing time in 3% NaCl solution.