Effect of pressure on solidification cracking susceptibility of Al–Si alloys

An approach was developed to calculate the crack susceptibility under various levels of pressure, and the corresponding numerical method was presented. The binary Al–Si alloy system was selected for study because the effect of high pressure on its phase diagram has been reported. The results showed a higher pressure can lead to a higher crack susceptibility and shift the most crack susceptible composition to higher solute contents. It was found a higher pressure can increase the effect of back diffusion on the solidification path and hence the crack susceptibility. This study provides a new understanding of the effect of pressure on solidification cracking susceptibility and can be a relevant starting point for studying solidification cracking under high pressures.