Properties of SnO-B2O3-SiO2 Lead-Free Glass Powder
- Source :
- Advanced Materials Research; November 2011, Vol. 412 Issue: 1 p133-137, 5p
- Publication Year :
- 2011
-
Abstract
- SnO-B<subscript>2</subscript>O<subscript>3</subscript>-SiO<subscript>2</subscript> glass powders, in which the different contents of SnO and B<subscript>2</subscript>O<subscript>3</subscript> were 35% ~ 70%wt and 26% ~ 61% wt respectively, were prepared through high-temperature melting, water quenching and Ball milling. XRD showed that the performance of forming glass was very good and the range of extension was very wide. The effect of the contents of SnO and B<subscript>2</subscript>O<subscript>3</subscript> on Tg, acidoresistant and density of prepared glass was studied. IR showed that it generates the heavy metal oxide generated glass. The density of glass powder decrease with increase of B<subscript>2</subscript>O<subscript>3</subscript> content, but increase with increasing SnO content. SnO-B<subscript>2</subscript>O<subscript>3</subscript>-SiO<subscript>2</subscript> glass had excellent chemical stability. Differential thermal analysis (DTA) shown that, with increasing SnO content, glass transition temperature first lower and then decreased.
Details
- Language :
- English
- ISSN :
- 10226680
- Volume :
- 412
- Issue :
- 1
- Database :
- Supplemental Index
- Journal :
- Advanced Materials Research
- Publication Type :
- Periodical
- Accession number :
- ejs26464811
- Full Text :
- https://doi.org/10.4028/www.scientific.net/AMR.412.133