Effects of ethylene polymerization conditions on the activity of SiO<INF>2</INF>-supported zirconocene and on polymer properties

The effects of polymerization conditions were evaluated on the production of polyethylene by silica-supported (n-BuCp)<INF>2</INF>ZrCl<INF>2</INF> grafted under optimized conditions and cocatalyzed by methylaluminoxane (MAO). The Al : Zr molar ratio, reaction temperature, monomer pressure, and the age and concentration of the catalyst were systematically varied. Most reactions were performed in toluene. Hexane, with the addition of triisobutilaluminum (TIBA) to MAO, was also tested as a polymerization solvent for both homogeneous and heterogeneous catalyst systems. Polymerization reactions in hexane showed their highest activities with MAO : TIBA ratios of 3 : 1 and 1 : 1 for the homogeneous and supported systems, respectively. Catalyst activity increased continuously as Al : Zr molar ratios increased from 0 to 2000, and remained constant up to 5000. The highest activity was observed at 333 K. High monomer pressures (≈ 4 atm) appeared to stabilize active species during polymerization, producing polyethylenes with high molecular weight (≈ 3 × 10⁵ g mol⁻¹). Catalyst concentration had no significant effect on polymerization activity or polymer properties. Catalyst aging under inert atmosphere was evaluated over 6 months; a pronounced reduction in catalyst activity [from 20 to 13 × 10⁵ g PE (mol Zr h)⁻¹] was observed only after the first two days following preparation. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 1987–1996, 1999