Effect of plasma on nitriding of Fe-18Cr-9Ni alloy

Abstract: The plasma nitriding behaviour of Fe-18Cr-9Ni alloy was compared with gas nitriding. The alloy was nitrided under the following conditions: specimen temperature: 823 K, nitriding time: mainly 108 ks, total pressure: 0.4–0.7 kPa, mixture ratio of N₂ and H₂∶ 0.25, discharge voltage: 350–450 V, current: 0.8–1.1 A. Formation of a surface layer of iron nitrides was not observed. Formation of a homogeneous internal nitriding layer, consisting of small precipitates of CrN and the γ-phase matrix, was, however, noted. The lattice constant at the specimen surface was smaller than that at greater depth. This may have been because the sputtering effect decreased the dissolved nitrogen content at the specimen surface. The sputtering of iron nitrides at the specimen surface by the plasma was experimentally confirmed through γ′-Fe₄N formation on Si beside an alloy specimen. The characteristics of the plasma nitriding mentioned above are discussed in relation to the sputtering.