Reactions of lead-free solders with CuNi metallizations

Abstract: We have done experimental research on the dissolution rate and intermetallic growth on Cu, Ni, and CuNi-alloy substrates as a function of time and Cu/Ni ratio of the substrate. Reactions that occur when CuNi metallizations are soldered with lead-free solders were investigated. The experiments were performed using Sn-3.5Ag and Sn-3.8Ag-0.7Cu solders and different CuNi alloys. To determine the rate of dissolution of the substrate material into the solder, CuNi foils of different concentrations were immersed in Sn-3.5Ag and Sn-3.8Ag-0.7Cu solder baths for soldering times ranging from 15 sec to 5 min at 250C. In addition, reflows of solder balls were made on top of bulk substrates to study the reaction when there is a practically infinite amount of CuNi available compared to the amount of solder. Thin film experiments were also done, where Ni containing under bump metallizations (UBMs) were fabricated and reflowed with eutectic SnAg solder balls. The nickel slows down the dissolution of the UBM into the solder and the formation of intermetallics during reflow compared to Cu metallizations. The solder/UBM interfaces were analyzed with SEM to find out how Ni concentration affects the reaction, and how much Ni is needed to obtain a sufficiently slow reaction rate.