Effect of the surface finish on the mechanical properties and cellular adhesion in (Ce,Y)-TZP/Al2O3 ceramic composites for denture implants.

Ceramic composites based on (Ce, Y)-TZP/Al 2 O 3 system have great potential for applications as dental implants due to their unusually great balance between good mechanical properties and resistance to hydrothermal degradation. Surface roughness plays an important role in controlling these properties, but few studies have investigated the relationship between cytocompatibility and surface roughness, at levels considered moderate and low, comparable to titanium implants. In this work, bending strength, hydrothermal degradation and biological evaluation of a ceramic composite based on (Ce,Y)-TZP/Al 2 O 3 system were investigated as a function of surface roughness. Compacted samples were sintered at 1500 °C - 2h and then submitted to different surface treatments: Group 1 composed of samples with smooth surfaces, Group 2 and Group 3 composed of rough surfaces (grinded with 15 μm or 45 μm diamond sandpaper, respectively. Samples were characterized by X-ray diffraction, scanning electron microscopy, contact angle and optical profilometry and then subjected to hydrothermal degradation tests in autoclave (134 °C - 2 bar) using artificial saliva. The Piston-on-three-balls (P–3B) testing was used to determine flexural strength. To assess indirect cytotoxicity, samples were immersed in the culture medium for NIH-3T3 cells for 72 h. Furthermore, cell adhesion and proliferation were investigated using MG63 cells (human osteosarcoma) after 3, 7, 14, and 21 days of culture. Cytotoxicity, adhesion, and cell proliferation were examined by the Methyl Tetrazolium salt (MTS) and Alizarin Red, using a confocal laser microscope. The results indicated that the materials have high resistance to degradation. Furthermore, the (Ce,Y)-TZP/Al 2 O 3 composites are not cytotoxic. The flexural strength of the composites was 913 ± 103 MPa in samples presenting original (smooth) surface, however, a reduction in the order of 17% was observed in samples containing rough surfaces. The rougher samples show the best cellular adhesion and proliferation, leading to the formation of a mineralized matrix after 21 days. These results clearly suggest that the new (Ce,Y)-TZP/Al 2 O 3 brand is strong and highly biocompatible and warrants further study. [ABSTRACT FROM AUTHOR]