Fatigue crack propagation of through cracks in thin sheets under combined traction and bending stresses.

ABSTRACT Fatigue crack propagation tests of through cracks in 3 mm thick aluminium alloy 6013-T6 plates, under combined membrane and bending stresses were carried out. Five different values for the ratio of bending to membrane stresses, SB, were examined: 0, 0.55, 1.25, 1.8 and 2.23. Firstly, the results were elaborated by taking into account only the membrane stress and the front dimension of the crack for the evaluation of the stress intensity factor range. The results relevant to the lower SB values, evaluated in this mode, show good agreement with the results obtained when only the membrane stress was applied, while the results obtained at the higher SB values exhibit a remarkable increase in the crack propagation rate. The results were successively evaluated on the basis of tabular stress intensity factor solutions available in the literature; the agreement between the predicted and the experimental data occurs when mean values of stress intensity factor, rather than local values, were used at the back face of the plate, i.e., the face where the bending produces a compressive stress, to counteract the high gradient of stress intensity factor present in this area. [ABSTRACT FROM AUTHOR]