Structural and magnetic properties of bulk MnBi permanent magnets.

Structural and magnetic properties of bulk nanostructural Mn100-xBix (x = 40, 45, 52) permanent magnets prepared by spark plasma sintering technique were studied. The effect of the Mn/Bi ratio on the MnBi low temperature phase (LTP) formation and its magnetic properties were investigated. An increase of the bismuth amount in the magnets leads to better formation of LTP, resulting in the improvement of both magnetization (Ms) and remanence (Mr), but decreasing the coercivity (Hc) of the magnets. At room temperature, Ms increases from 27.87 emu/g for Mn60Bi40 to 45.31 emu/g for Mn48Bi52, whereas Hc decreases from 12 to 7.9 kOe. The microstructure of Mn48Bi52 magnet is composed of fine and uniform grains with an average size of 140 nm as shown in the TEM image. The Mn48Bi52 magnet shows a high Hc of 19 kOe at 423 K, indicating a strong positive temperature coefficient of coercivity for the MnBi magnet. [ABSTRACT FROM AUTHOR]