Composition Effects on the Critical Current of MOCVD-Processed Zr:GdYBCO Coated Conductors in an Applied Magnetic Field.

Zr:GdYBCO films were grown by reel-to-reel metal organic chemical vapor deposition (MOCVD) on hastelloy tapes with IBAD-MgO-based buffer. The composition was varied systematically to investigate the effects of changes in (Gd+Y)/Ba, (Gd+Y)/Cu and Gd/Y ratios and Zr-doping concentration on the critical current density (Jc) of the films in an applied magnetic field (B). The magnetic-field-angle dependence of Jc measured at 77 K and 1 T showed that (1) for Gd+Y content ranging from 1.2 to 1.5, the minimum Jc for any angle did not vary significantly with the Gd+Y content; while the Jc at B//c varied significantly and took its maximum value at Gd+Y content of 1.2; (2) increasing Gd+Y could suppress or level off the Jc peak at B//c which was associated with the pinning from BaZrO3 nano-columns; (3) the optimum Zr-concentration for the highest Jc(77\ \rm K,1\ \rm T) is in the range of 0.04–0.07 in the film; in this range under certain growth condition, the c-peak in the angular dependence of Jc could be higher than the ab-peak; (4) increasing Gd/Y ratio increased Jc\_\min(77\ K,1\ T); (5) in self-field or low field, however, the optimized Gd/Y ratio was about 1. [ABSTRACT FROM AUTHOR]