Influence of the thickness of sputter-deposited platinum films on the electrochemical promotion of propane combustion.

8 to 120 nm-thick Pt coatings were sputter-deposited on Yttria-Stabilised Zirconia (YSZ) membranes, 17 mm in diameter, by magnetron sputtering of a Pt target at low pressure (0.3 Pa). The catalytic activity of propane combustion under open-circuit conditions is first measured near to the stoichiometry (0.2%C₃H₈/1%O₂) and shows that the coatings present a rather high catalytic activity. Close-circuit measurements were finally performed at 337 °C and 400 °C. They show that rather high faradaic efficiencies in the range 10⁶ can be reached as soon as the Pt film is thick enough to allow a bias of its whole area. [ABSTRACT FROM AUTHOR]