Effect of homogenization temperature on microstructure and mechanical properties of low-carbon high-boron cast steel.

The effects of quenching treatment on the microstructure, hardness, impact toughness, and wear resistance of low-carbon high-boron cast steel (LCHBS) containing 0.15–0.3 %C, 1.4–1.8 %B, 0.3–0.8 %Si, 0.8–1.2 %Mn, 0.5–0.8%Cr, 0.3–0.6%Ni, and 0.3–0.6%Mo have been investigated by optical microscopy (OM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM), and via an electron probe microanalyzer (EPMA), X-ray diffraction (XRD) analysis, impact tester, hardness tester, and wear tester. The as-cast matrix of LCHBS consists of pearlite and ferrite. There is 8–10 vol.% Fe₂(B, C) type borocarbides in the matrix. The micro-hardness of Fe₂(B, C) is 1430–1480 Hv. Fe₂(B, C) shows no obvious change and the matrix completely transforms into lath martensite upon quenching at 900 °C to 1100 °C. The microhardness of the matrix and the macrohardness of the LCHBS sample show a slight increase with an increase of homogenization temperature. When the homogenization temperature exceeds 1050 °C, no distinct change in the hardness is observed. The change of homogenization temperature has no apparent effect on the impact toughness of LCHBS. The mass losses of LCHBS increase distinctly when the wear load increases. The homogenization temperature is less than 1000 °C and the wear rate of LCHBS decreases with an increase of temperature. The wear rate does not display any obvious change after exceeding a homogenization temperature of 1000 °C. [ABSTRACT FROM AUTHOR]