The impact of vacuum freeze-drying on collagen sponges after gas plasma sterilization.

The sterilization of porous collagen sponges remains a challenging procedure. Gamma irradiation denatures collagen, resulting in dramatic changes to its structure. Ethylene oxide leaves toxic residues requiring weeks to evaporate. This study investigated the impact on cell behavior of gas plasma treatment when combined with vacuum freeze-drying. The goal of this procedure is to eliminate the molecules of hydrogen peroxide remaining after the sterilization process, together with their decomposition products, from the scaffolds. These molecules hinder the immediate use of the porous designs. Collagen and EDC/NHS-heparinized collagen scaffolds were sterilized with gas plasma. H₂O₂ released by the collagen specimens was measured by peroxidase test both immediately and also 1 week after the plasma treatment. Further measurements were done 24, 36, 48 and 72 h after vacuum freeze-drying. The activity of these scaffolds was further evaluated in relation to the proliferation, migration and differentiation of human umbilical vein endothelial cells (HUVECs). Both immediately after exposure to gas plasma and also 1 week later, the collagen designs contained significantly higher concentrations of H₂O₂ than scaffolds having also undergone vacuum freeze-drying. This procedure achieved faster decontamination of the remaining H₂O₂. Following vacuum freeze-drying, sponges already allowed HUVEC proliferation after 48 h, but in non-lyophilized specimens after gas plasma treatment alone, cell death occurred as early as only 1 week later. These data highlight the advantages of carrying out vacuum freeze-drying following gas plasma sterilization. The results show the substantial impact of sterilization of porous materials made for tissue engineering. [ABSTRACT FROM AUTHOR]