The Effect of μ-Limestone Additions on the Mechano-Chemical and Microstructural Properties of Slag and Binary Slag/Ground Fly Ash Alkaline-Activated Binders.

An alternative approach to reducing the clinker factor, i.e., worldwide CO₂ emissions resulting from the production of composite cement, is to replace these materials with supplementary aluminosilicate-based materials that promote the formation of alkali-activated cements, whose elevated temperature resistance, limited permeability, strong binding properties, excellent durability, high chemical corrosion resistance, confinement of toxic waste, and environmentally low impact have attracted a lot of attention in the cement industry. The principal aluminosilicate-based supplementary materials (SCMs) used in the cement industry are fly ash and blast-furnace slag. Recently, limestone has been proposed for use in alkali-activated cement to improve mechanical resistance and promote nucleation sources for the hydration of hybrid gels. In the current research work, the effect of 5 and 10 wt% limestone additions to slag and fly ash/slag alkali-activated cements with NaOH-4M was studied to evaluate the mechano-chemical and microstructural properties of alkali-activated cement. The effect of limestone was studied using mechanical resistance, XRD, FTIR, SEM-EDS, and calorimetry methods. The XRD, FTIR, and SEM-EDS results demonstrated the formation of portlandite Ca(OH)₂ after the activator solution's reaction with limestone. The limestone's dissolution in Ca²⁺ contributes to hybrid gel formation ((N, C)-A-S-H, N-A-S-H, and C-A-S-H), resulting in compressive strength higher than 20 MPa, the recommended resistance for commercial cement. [ABSTRACT FROM AUTHOR]