Synthesis of a Hard Anodic Oxide Coating with a Structure Allowing for Its Modification by Nanoparticles.

A hard anodic oxide coating's characteristic porous structure allows for its modification by the incorporation of nanoparticles. However, achieving an appropriate microstructure requires an optimal pore arrangement and shape, which is influenced by the electrolyte composition, current densities, temperature, and processing time. To achieve pores with a diameter of about 50 nm and the most regular structure, a range of these parameters were tested. Using a two-stage manufacturing process had a beneficial effect on increasing the microporosity of the coating. The addition of phthalic acid at 0 °C did not increase the pore diameter, but allowed for the process to be carried out at higher temperatures. However, the coating produced at 20 °C had a larger pore diameter, but numerous defects. The coating obtained from the three-component solution had the most regular structure, but the smallest pore diameter. [ABSTRACT FROM AUTHOR]