Mullite Synthesis Using Porous 3D Structures Consisting of Nanofibrils of Aluminum Oxyhydroxide Chemically Modified with Ethoxysilanes.

Nanocrystalline mullite was synthetized by annealing a highly porous 3D structure consisting of nanofibrous aluminum oxyhydroxides treated with ethoxysilanes. The chemical, structural, and phase transformations in the aluminosilicate nanosystem were studied in the temperature range between 100 and 1600 °C. The features of the solid-phase synthesis of mullite at the interface of crystalline alumina with a liquid silica layer are discussed. It was established that chemical modification of the alumina surface with ethoxysilanes significantly limits the interphase mass transport and delays the phase transformation of the amorphous oxide into γ-Al₂O₃, which begins at temperatures above 1000 °C, while the basic structural nanofibrils are already crystallized at ~850 °C. The formation of mullite was completed at temperatures ≥ 1200 °C, where the fraction of γ-Al₂O₃ sharply decreased. [ABSTRACT FROM AUTHOR]