Comparative analysis of 3D-printed and freeze-dried biodegradable gelatin methacrylate/ poly‐ε‐caprolactone- polyethylene glycol-poly‐ε‐caprolactone (GelMA/PCL-PEG-PCL) hydrogels for bone applications.

Gelatin methacrylate (GelMA) is a photo-cross-linkable biopolymer. A combination of GelMA with biodegradable polyesters such as PCL (poly‐ε‐caprolactone) and their triblock derivatives improve the mechanical properties of GelMA. PCL-PEG-PCL (PCEC) was synthesized using ring-opening polymerization of ε-caprolactone in the presence of polyethylene glycol (PEG). The GelMA- PCEC was fabricated using freeze-drying and 3D printing and their porosity, mechanical properties, and swelling behavior were investigated. Human dental pulp stem cells were cultured on the scaffolds for a period of 14 days and cell adhesion was evaluated by scanning electron microscopy. Cell viability was analyzed by MTT and osteogenic differentiation was evaluated by Alizarin red S. Results showed that the 3D-printed scaffold had higher water absorption rate, retaining its structure up to a strain of 0.2 %, and a higher Young's modulus compared to the freeze-dried scaffold. In terms of cell viability, the 3D-printed scaffold outperformed the freeze-dried scaffold with a percentage of 86 % and 63 % viability respectively. Moreover, the 3D-printed scaffold exhibited better osteodifferentiation with calcium deposition. Overall, these findings suggest that the 3D-printed scaffold may have advantages over the freeze-dried scaffold in tissue engineering applications that require high water absorption, elasticity, and cell viability. The fabricated scaffolds provided suitable cell proliferation. [ABSTRACT FROM AUTHOR]