Influence of Steel and Poly Vinyl Alcohol Fibers on the Development of High-Strength Geopolymer Concrete.

The present study focuses on the mechanical performance of steel and polyvinyl alcohol fibers embedded in the geopolymer matrix. A high-strength geopolymer concrete with fly ash, slag and silica fume as precursors and sodium hydroxide and sodium silicate solutions as activators has been tested for its strength in compression and flexure. The influence of fibers on flowability, long-term shrinkage and sulphuric acid attack on the geopolymer concrete has also been studied. The dosage of fibers was maintained at 1%, 2% and 3% by volume, and fibers of length 13 mm have been used in the study. Results indicate that slag with 3% steel fibers by volume had a predominant influence on the strength development of steel fiber-reinforced geopolymer concrete, yielding a compressive strength of 107 MPa after 28 days. Blast furnace slag resulted in increasing the shrinkage of concrete due to rapid gel formation owing to the presence of calcium ions, although the fibers helped reduce the shrinkage to some extent. The strength of steel fiber geopolymer concrete was superior to PVA fiber geopolymer concrete; however, after an acid attack, the strength of steel fiber geopolymer concrete was reduced more than PVA fiber geopolymer concrete due to the enhanced corrosion resistance of PVA fibers. [ABSTRACT FROM AUTHOR]