Exploring the potential of dual‐metallized PET towards improving the efficiency of outermost reflective layer in fire proximity clothing.

The outermost layer of a fire proximity suit needs to conform to a strict requirement of radiant protection performance (RPP) ≥ 20s, which is indicative of its ability of offering a protection for at least 20s duration from second degree burn upon radiant heat exposure (84 kW/m2). Typically, this layer is fabricated by laminating a single‐side metallized PET (SMPET) layer with glass fabric. However, upon erosion of the deposited metal, this laminate is rendered unsuitable due to loss of reflectivity. Here, we explore the possibility of replacing the SMPET with its dual‐metallized analogue (DMPET) and determine the effect of increasing the optical density (OD) on the adherence and protection level. Metallized films with OD varying from 2.2 to 4.8 were laminated with glass fabrics of twill, satin and plain weave pattern using a silicone adhesive. The peel adhesion strength of laminates prepared using DMPET was found to be higher (1.01 ± 0.03 N/mm), as compared to SMPET (0.63 ± 0.03 N/mm) and the resulting films did not undergo delamination during flexing. Laminates prepared from satin woven glass fabric exhibited lowest flexural rigidity followed by twill and plain woven glass fabric. Protection offered by the laminate from convective heat was quantified in terms of the thermal protective performance (TPP), and the abraded laminate prepared using DMPET (OD‐4.8) was found to meet all the mandatory requirements of proximity clothing, offering an RPP of 27 s and a TPP of 62 cal/cm2 s. In comparison, SMPET laminates exhibited lower level of adhesion and offered an RPP of only 7.5 s. [ABSTRACT FROM AUTHOR]