Recycling of Waste Granodiorite Powder as a Partial Cement Replacement Material in Ordinary Concrete.

In this study, the effect of using waste granodiorite powder (WGP) as a cement replacement material in percentages ranging from 1 to 9% on various physical and mechanical properties of ordinary concrete was investigated. The resistance of produced concretes with WGP to the high temperature effects on the 28 days compressive strength were studied as well. Granodiorite is one of the well-known igneous rocks that have been used in previous research as a replacement for coarse or fine aggregates due to the hardness of its grains. However, rare studies have investigated its powder as a partial cement replacement material. Results showed the ability of investigated WGP with high surface area to act as a supplementary cementitious material that contributed to enhance the results of mechanical and physical properties of concrete. At traditional room temperature, the optimal replacement percentage was 7%, where the 28 days compressive and tensile strengths were improved by 28.3% and 17.3%, respectively. The optimal replacement ratio varied between 7 and 9% in the case of high temperatures, according to exposure time and temperature degree. Statistical and sensitivity analysis was conducted on 66 available compressive strength value represents all variables before and after elevated temperature exposure. While the regression equation showed good R² value of 85.3%, sensitivity analysis indicated that compressive strength value is most sensitive to temperature, followed by WGP ratio and exposure time, with importance values of 56, 26, and 18 %, respectively. Results showed also that the setting times and consistency was decreased with increasing the replacement ratio with WGP, while the workability was slightly improved up to 5% replacement ratio. Furthermore, microstructure analysis showed that WGP can help to densify the concrete matrix due to its small size and ability to fill the interstitial voids in the concrete matrix. [ABSTRACT FROM AUTHOR]