Effects of Compound Use of Two UV Coating Microcapsules on the Physicochemical, Optical, Mechanical, and Self-Healing Performance of Coatings on Fiberboard Surfaces.

Ultraviolet (UV) coatings are widely used because of their good performance. However, the self-healing performance of UV coatings can be further improved. Microcapsule technology can be used to solve this problem. To investigate the effects of the compound use of two UV coating microcapsules on coatings of a fiberboard surface, three kinds of UV primer microcapsules (1#, 2#, and 3# microcapsules) with different contents were added to a UV primer, and a UV top coating was prepared with UV top coating microcapsules at a consistent ratio. The UV coating was used to coat the fiberboard surface by way of a two-primer and two-top coating method. The results show that as the content of the UV primer microcapsules was increased, the self-healing rates of all three groups of coatings increased and later decreased. The color difference ΔE of coatings with the content of the UV primer microcapsules at 4.0% and top coating microcapsules at 6.0% was 3.59, the gloss was 1.33 GU, the reflectance was 21.17%, the adhesion grade was 2, the hardness was 2H, the impact resistance grade was 5, the roughness was 1.085 μm, and the self-healing rate was 30.21%. Compared with the self-healing rate of the blank control group, the increase in the self-healing rate was 10.07%, and the improvement rate was 50.00%. The comprehensive performance of the coating was better. The results provide a technical reference for the application of the UV coating microcapsules in the UV coating on fiberboard surfaces. Incorporating the self-healing UV coating microcapsules into the UV coatings and applying the UV coating microcapsules on the fiberboard surfaces supports the microcapsule technology of self-healing UV coatings, lays the foundation for extending the service life of furniture while improving the furniture's quality, and promotes the sustainable development of the coating industry. [ABSTRACT FROM AUTHOR]