Dispersed CeO 2 Nanorods with Low-Speed Mixing for Mechanical Properties Promotion of PTA Steel Coatings.

The plasma-transferred arc technology has been observed to induce preferential grain orientation in multiple directions, leading to nonuniform grain growth within the alloy coating material. The addition of nano-oxides can act as heterogeneous nucleation sites, reducing the preferred orientation of grains. In this study, a low-speed mixing method was employed to coat highly dispersed CeO₂ nanorods (CNRs) onto the surface of 14Cr2NiSiVMn alloy powder particles. The aim was to analyze the influence of dispersed CNRs on grain growth orientation in different directions and the refinement and heterogeneous nucleation effect of CNR additives. The addition of 0.5 wt.% CNRs resulted in the refinement of dendritic grains along both the perpendicular and parallel directions to the coating cladding direction, leading to the formation of more uniform equiaxed crystals. The combination of Ce with Si and V elements formed submicron particles, which promoted grain nucleation and reduced defects in the coating. Consequently, the mechanical performance of the sample significantly improved. In the deposition direction, there was a notable improvement in microhardness (20.4%), tensile strength (97.6%), and elongation (59.0%). In the perpendicular deposition direction, the tensile strength increased by 88.1%, and the elongation increased by 33.9%. Additionally, the weight loss due to wear decreased by 44.2%, and the relative wear resistance improved by 79.3%. [ABSTRACT FROM AUTHOR]