Duplex stainless steel 2209 with excellent properties deposited by plasma arc additive manufacturing without post heat-treatment: favorable phase ratio and no σ-phase.
- Source :
- Archives of Civil & Mechanical Engineering (Elsevier Science); Jul2024, Vol. 24 Issue 3, p1-12, 12p
- Publication Year :
- 2024
-
Abstract
- This paper utilizes the plasma arc as the heat source to successfully fabricate well-formed thin-walled parts using combined cable wire duplex stainless steel 2209. Microstructure of parts exhibited the favorable two-phase ratio and the absence of σ-phase. It was found that appropriate heat input (1.68 kJ/cm) and cooling rate (5 °C/s) can effectively avoid the precipitation of σ-phase. Furthermore, the properties of the as-deposited samples were comparable to those of the samples heat-treated at 1300 °C, proving that no subsequent heat treatment was required for 2209 stainless steel fabricated by plasma arc additive manufacture. The samples showed excellent properties, in which the ultimate tensile strength and yield strength were improved by about 7% and 24% compared with GB/T4237-2015. The impact toughness meets the requirements of EN10028-7-2016, which is about 35% higher than that of the cold metal transfer samples, and the corrosion resistance is comparable to that of hot rolled 2205. [ABSTRACT FROM AUTHOR]
Details
- Language :
- English
- ISSN :
- 16449665
- Volume :
- 24
- Issue :
- 3
- Database :
- Complementary Index
- Journal :
- Archives of Civil & Mechanical Engineering (Elsevier Science)
- Publication Type :
- Academic Journal
- Accession number :
- 177897548
- Full Text :
- https://doi.org/10.1007/s43452-024-00907-8