Effect of Grafting Treatment on Properties of Aramid Fiber/Carbon Black/Styrene-Butadiene Rubber Composites.

Authors :
LI Yang
XIAO Zhen
SHI Cai-wen
PAN Xiao-li
WANG Zi-yi
Source :
Plastics Science & Technology / Suliao Ke-Ji; 2024, Vol. 52 Issue 3, p67-71, 5p
Publication Year :
2024

Abstract

In this paper, the aramid fiber was modified with polyamic acid (PAA) and glycidyl polyhedral sesquioxane (POSS) by supercritical CO<subscript>2</subscript> assisted solution impregnation method, and then aramid fiber/carbon black/styrene-butadiene rubber composites (AF/CB/SBR=2/50/100) were prepared by modified aramid fiber. The effects of modified aramid fibers on the processing performance of composites were tested and the effects of two surface grafting agents on the performance of AF/CB/SBR composites were investigated. The results showed that the crosslinking density of the composites increased significantly after the modification of POSS and PAA with supercritical CO<subscript>2</subscript>, which delayed the vulcanization process and increased the positive vulcanization time. The tensile strength and 100% constant elongation of the composites modified by supercritical CO<subscript>2</subscript>-assisted POSS increased by 10.77% and 19.58%, respectively, while the tensile strength and 100% constant elongation of the composites modified by supercritical CO<subscript>2</subscript>-assisted PAA increased by 15.13% and 25.77%, respectively. Correspondingly, after the modification of POSS and PAA assisted by supercritical CO<subscript>2</subscript>, the interface slip energy values were 5.76 and 6.94, increasing by 17.6% and 41.6%, respectively. In comparison, the aramid fiber modified by macromolecule PAA grafting is more favorable to the improvement of the comprehensive properties of rubber composites. [ABSTRACT FROM AUTHOR]

Details

Language :
Chinese
ISSN :
10053360
Volume :
52
Issue :
3
Database :
Complementary Index
Journal :
Plastics Science & Technology / Suliao Ke-Ji
Publication Type :
Academic Journal
Accession number :
177628203
Full Text :
https://doi.org/10.15925/j.cnki.issn1005-3360.2024.03.013