Mechanical, thermal, and morphological properties of poly(3-hydroxy butyrate) nanocomposites prepared by melt mixing method.

This research focuses on the preparation of poly (3-hydroxy butyrate) (PHB) nanocomposites using the melt mixing method. Two types of organically modified nanoclay, Cloisite 93A (C93A), and Cloisite 30B (C30B), were incorporated at various weight percentages into the PHB matrix to create the nanocomposites. Comparative analyses were conducted between PHB/C93A and PHB/C30B to assess their tensile and impact properties in relation to the matrix polymer. Between the nanocomposites, the PHB/C93A nanocomposites shows an optimum tensile modulus of 949 Mpa with a 3 wt% clay loading, while PHB/C30B nanocomposites demonstrated improved percentage elongation at break of 5.33 % and enhanced Izod impact strength of 39.67 J/m at 3 wt% of clay load. The thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) signifies the thermal behavior of both the matrix and nanocomposite. The degree of crystallinity is observed to be 47 % in case of the PHB/C30B nanocomposites as compared to the PHB/C93A nanocomposites as 38 %. Again in case of thermogravimetric analysis (TGA), the maximum % char of 5.198 is observed for the PHB/C30B nanocomposites. The enhanced viscoelastic behavior of the PHB/C93A nanocomposites was attributed at a peak of approx. 55–60 °C due to the incorporation of C93A nanoclay into the matrix in the study of dynamic mechanical analysis (DMA). The morphological investigation using WAXD analysis showcased particle clay intercalation and dispersion within the PHB matrix, indicating effective clay-matrix interactions. Overall, this study sheds light on the enhanced properties of PHB nanocomposites with the incorporation of organoclay, offering potential applications in various industries. [ABSTRACT FROM AUTHOR]