FDM 型3D プリンタ成形s-CF/PA6 積層材の モードI 層間破壊靭性評価.
- Source :
- Journal of the Japanese Society for Experimental Mechanics; 2023, Vol. 23 Issue 2, p152-159, 8p
- Publication Year :
- 2023
-
Abstract
- This study evaluated the Mode I interlaminar delamination fracture toughness of s-CF/PA6 (short Carbon Fiber/Polyamide 6) laminates molded by FDM (Fused Deposition Molding) type 3D printer, using DCB (Double Cantilever Beam) tests on two different configurations. We also tested and compared dried and undried specimens. Fracture surface observations by scanning electron microscope revealed the mechanism of toughness development and factors affecting interlaminar delamination fracture toughness. The results showed that angle ply exhibit higher toughness than cross ply. The toughness of dried specimens was higher than that of the non-dried specimens. These results were highly variable. One reason for this is the difference in adhesion states and voids between layers. One possible cause of insufficient welding is a molding area temperature during molding. In addition, insufficient welding may occur if the filaments are printed when they are not sufficiently dry. As for voids, there is a possibility that they can be improved by adjusting the 3D printer. [ABSTRACT FROM AUTHOR]
Details
- Language :
- Japanese
- ISSN :
- 13464930
- Volume :
- 23
- Issue :
- 2
- Database :
- Complementary Index
- Journal :
- Journal of the Japanese Society for Experimental Mechanics
- Publication Type :
- Academic Journal
- Accession number :
- 173872195