Scaling up of Growth, Fabrication, and Device Transfer Process for GaN‐based LEDs on H‐BN Templates to 6‐inch Sapphire Substrates.

The growth of hexagonal boron nitride (h‐BN) and van der Waals (vdW) epitaxy of blue multi‐quantum well (MQW) GaN‐based LED heterostructures on 6‐inch sapphire substrates using metal‐organic chemical vapour deposition (MOCVD) is demonstrated. Challenges associated with the growth of large surface h‐BN and the subsequent vdW epitaxy of GaN‐based LED heterostructures are discussed. To overcome these challenges, the spatial uniformity is controlled of the growth temperature, optimizes the slope of temperature variations during the growth and cooling process, and manages the surface temperature during switching of gas flows. With these adaptations, high quality GaN‐based LED heterostructures are grown on h‐BN without any spontaneous delamination. The GaN‐based LED devices are then fabricated on a 6‐inch sapphire wafer, which are lifted off as a membrane and transferred to a flexible copper support. These GaN‐based LED devices emitt bright blue illumination with an electroluminescence peak at 437 nm. This scaling up of growth, lift‐off, and transfer can lead to the commercialization of GaN‐based LEDs on h‐BN template on 6‐inch sapphire substrates, with a process compatible with current modern equipment for the fabrication of LEDs and electronic devices. [ABSTRACT FROM AUTHOR]