Fabrication, Characterization, and Corrosion Protection of Siloxane Coating on an Oxygen Plasma Pre-treated Silver-Copper Alloy.

In this study, siloxane has been used for the protection of metal artifacts from corrosion in the form of transparent barrier coating films because of their good adhesion to the metal substrate. The effect of oxygen plasma pre-treatment on the adhesion properties of the siloxane thin film on the silver-copper alloy substrate was investigated. Radiofrequency plasma-enhanced chemical vapor deposition (RF-PECVD) was used for the deposition process. Surface identification and characterization of the deposited films were carried out using Scanning Electron Microscopy coupled with energy-dispersive x-ray spectroscopy (SEM–EDX) and Fourier-transform infrared spectroscopy (FT-IR). Surface topography and roughness were investigated by atomic force microscopy (AFM). The hydrophobic characteristic was measured by water contact angle measurement (WCA). The film thickness was evaluated using a spectroscopic ellipsometer (SE). Colorimetric measurement (CM) was used to evaluate changes in the appearance of the surface following the PECVD deposition of the SiO₂ protective layer. The corrosion protection ability of siloxane films for metal substrates as a function of RF power and gas feed composition was examined by the electrochemical impedance spectroscopy (EIS) technique. It was found that the deposited film improved the protective efficiency for samples from 55.29 to 92.93%. Besides, after the oxygen plasma pretreatment step, the film showed better corrosion resistance of the tested samples. [ABSTRACT FROM AUTHOR]