Kenaf Fiber and Hemp Fiber Multi-Walled Carbon Nanotube Filler-Reinforced Epoxy-Based Hybrid Composites for Biomedical Applications: Morphological and Mechanical Characterization.

This study used a hybrid combination of kenaf and hemp fibers and the multi-walled carbon nanotube (MWCNT) reinforcements in the matrix phase to synthesize the composites. A kenaf/hemp fiber blend with MWCNTs in epoxy was used for the specific concentration. The procedure used three composite materials chosen from pilot trials. The ratio of MWCNT filler particles was altered up to the agglomeration limit based on initial trials. Two specimens (2 and 3) were supplemented with MWCNTs in a concentration range of 0.5 wt. % to 1 wt. %, with the fiber concentration being maintained in equilibrium with the epoxy resin, all of the materials were tested under the same conditions. The hybrid nanocomposite was characterized for its morphological and mechanical properties; the tensile properties were higher for 1% MWCNTs concentration (specimen 2), while the flexural properties were higher for 0.5% MWCNTs, with values of 43.24 MPa and 55.63 MPa, correspondingly. Once the MWCNT concentration was increased to 1 wt. %, the maximum impact strength was achieved (specimen 3). In the limits of the Shore-D scale, the kenaf fiber and hemp fiber matrix composite (specimen 1) gained a hardness index of 84. Scanning electron microscopy was carried out to analyze the morphological features of the fractured samples and to assess the adhesion between the fiber, matrix, and surface. Among the various fillers tested, the kenaf fiber/hemp/MWCNT composite (specimen 3) demonstrated superior binding and reduced the incidence of fiber pull-out, breakage, and voids. In addition to the comparative analysis, the addition of 0.5 wt. % MWCNTs resulted in better mechanical properties compared to the other two combinations. [ABSTRACT FROM AUTHOR]