Laser Conditioning: A Preferred Option Over Conventional Acid Etching for Orthodontic Bonding.

Aim: To evaluate the demineralization resistance and the shear bond strength of enamel surfaces after erbium, chromium: yttrium-scandium-gallium-garnet (Er, Cr:YSGG) laser etching (2 W/15 Hz, 2 W/25 Hz) and to compare them with conventional acid etching for orthodontic bonding. Materials and Methods: A total of 60 extracted human premolars with intact enamel surface were used for this study. Demineralization Resistance was estimated using ion-coupled plasma atomic emission spectrometer (ICP-AES). Shear bond strength was evaluated using Universal Testing Machine--Instron. Results: Statistically significant difference (P < .001) was found in the concentration of dissolved calcium (Ca) and phosphorus (P), with the highest mean Ca and P in the acid-etched group, followed by 2 W/15 Hz laser-etched group and least with 2 W/25 Hz laser-etched group. Maximum bond strength was found in the acid-etched group (12.06 MPa), followed by the 2 W/25 Hz laser-etched group (9.01 MPa) and 2 W/15 Hz laser-etched group (8.39 MPa). The differences were statistically significant. Conclusions: Laser conditioning of enamel surface revealed significant demineralization resistance with a minimal dissolution of Ca and P ions in the demineralizing solution. Moreover, optimum bond strength was obtained similar to that of acid etching; hence, Er,Cr:YSGG laser conditioning of enamel surface is preferred over the conventional phosphoric acid etching for orthodontic bonding. [ABSTRACT FROM AUTHOR]