Study on the Strength Evolution Characteristics of Cemented Tailings Backfill from the Perspective of Porosity.

At present, the filling mining method is widely used. To study strength evolution laws of cemented tailings backfill (CTB) under different curing ages, in the experiment, mine tailings were used as aggregates, ordinary Portland cement (PC32.5) was used as cementing materials, and different additives (lime and fly ash) were added to make filling samples with the solids mass concentration at 74% and the cement-sand ratios 1:4, 1:6 and 1:8. Based on the nuclear magnetic resonance (NMR) technology, the porosity test of filling samples with curing ages of 3 d, 7 d and 28 d was carried out, and the uniaxial compressive strength test was carried out on the servo universal material testing machine. The relationship between the uniaxial compressive strength and porosity of backfills and the curing age in the three groups was studied, and change laws of the porosity variation and strength growth rate of backfills were analyzed. Based on the variation in porosity, the strength evolution model of the CTB under different curing ages was established, and the model was fitted and verified with test data. Results show that the uniaxial compressive strength, porosity, porosity variation, and strength growth rate of the three groups of backfills gradually increase with the increase of the curing age, the porosity of backfill basically increases with the decrease of the cement–sand ratio, and the porosity of backfill decreases with the increase of the curing age. Porosity variations and relative strength values of the three groups of backfills under different cement-sand ratios obey an exponential function, and the two have a good correlation, indicating that the established filling strength evolution model can well reflect strength evolution laws of the CTB with the change of curing age. [ABSTRACT FROM AUTHOR]