Structural and Mechanical Properties of the ZrC/Ni-Nanodiamond Coating Synthesized by the PVD and Electroplating Processes for the Cutting Knifes.

In this work, combined gradient ZrC/Ni-nanodiamond ultradispersed diamonds (UDD) coatings were synthesized on the surface of knife blades made of hard alloy WC-2 wt.% Co by electroplating and cathode arc evaporation PVD techniques to increase the durability period of a wood-cutting milling tool. The microstructure, phase and elemental composition, microhardness, and adhesion strength of the coatings were investigated. Ni-UDD layer is not mixed with the ZrC coating and hard alloy substrate. Cobalt is present in Ni-UDD layer after deposition of ZrC. The ZrC/Ni-nanodiamond coating consists of separate phases of zirconium carbide (ZrC), α-Ni, and Ni-UDD. The maximum value of microhardness of the Ni-nanodiamond coating is 5.9 GPa. The microhardness value of the ZrC/Ni-nanodiamond coatings is 25 ± 6 GPa, which corresponds to the microhardness of the hard alloy substrate and ZrC coating. The obtained high values of the critical loads on the scratch track of the ZrC/Ni-nanodiamond coating in 24 N prove a sufficiently high value of the adhesion strength of the bottom Ni-UDD layer with WC-Co substrate. Pilot testing of ZrC/Ni-nanodiamond-coated cutting tools proved their increasing durability period to be 1.5-1.6 times higher than that of bare tools, when milling laminated chipboard. [ABSTRACT FROM AUTHOR]