High-Temperature Tribological Behavior of Al-20Si-5Fe-2Ni/ZrB2 Composites.

In this work, Al-20Si-5Fe-2Ni/ZrB₂ composites with 0-20 wt% ZrB₂ were fabricated by spark plasma sintering. The effects of ZrB₂ content on the microstructure, mechanical properties and high-temperature tribological behavior of the composites were investigated. The results indicate that Si, Al₅FeSi, and ZrB₂ particles are uniformly distributed in the aluminum matrix. The density, hardness, and compressive strength increase with increasing ZrB₂ content. The friction coefficient and wear rate are dependent on the ZrB₂ content and test temperature. At a certain temperature, the friction coefficient increases with an increase in ZrB₂ content, whereas the wear rate shows a reverse trend. Due to the improvement in thermal stability and high-temperature softening resistance, the composite shows improved wear resistance and increased transition temperature from mild wear to severe wear. [ABSTRACT FROM AUTHOR]