Comparative Study of GdLu2Al2Ga3O12:Ce and GdY2Al2Ga3O12:Ce Scintillation Crystals for $\gamma$ -Ray Detection.

The scintillation characteristics of Czochralski-grown GdLu2Al2Ga3O12:Ce and GdY2Al2Ga3O12:Ce single crystals were compared for $\gamma$ -ray detection. At 662-keV $\gamma$ -rays, light yield (LY) of 30700 photons/MeV obtained for GdLu2Al2Ga3O12:Ce is higher than that of 27200 photons/MeV obtained for GdY2Al2Ga3O12:Ce, while its energy resolution is inferior (14% versus 10.6%) due to a larger nonproportionality of LY. Scintillation decays were measured using the time-correlated single photon counting technique. A fast component decay time of 48 ns with relative intensity of 71% obtained for GdLu2Al2Ga3O12:Ce is superior to that of 106 ns (57%) for GdY2Al2Ga3O12:Ce. The coincidence time spectrum was measured in reference to a fast BaF2 scintillator, and coincidence time resolution was discussed. [ABSTRACT FROM AUTHOR]