Microstructural and Mechanical Studies of T91/T22 Welded Joints.

Comparative studies have been performed to decide an appropriate combination of welding process and filler material by virtue of microstructural evolution, micro-hardness studies, tensile strength and fractographic analysis. Manual arc welding and tungsten inert gas welding processes are used along with different filler materials to manufacture T91/T22 welded joints. Studies with the purpose of comparison and evaluation of different zones of the weldments have been carried out. The highest value of micro-hardness observed on the T91 HAZ of the weldments may be attributed to martensitic structure of the region. The fracture morphology of both the weldments obtained from T22 BM has revealed the ductile fracture. Comparatively higher tensile strength (578 MPa) of T91/T22, GTAW combination is noticed by virtue of lower heat input. The better performance of T91/T22, GTAW weldment can be quoted on the basis of better joint integrity, tensile strength and ductility (26.4%). [ABSTRACT FROM AUTHOR]