Characterization of Ni/Ce Co-Doped BST Thin Film Grown on LSCO/Pt Electrodes Prepared by Pulsed Laser Deposition.

Perovskite (Ba 0.6 Sr 0.4 )TiO 3 (BST) thin films doped with Ni, Ce and Ni/Ce codopants were prepared on LSCO/Pt/SiO 2 /Si substrates by pulsed laser deposition method. In this study, La 0.5 Sr 0.5 CoO 3 (LSCO) bottom electrodes were used to improve the crystallinity and dielectric properties of BST films. Single ion doped(1 mol%Ni doped,1 mol%Ce doped) BST films showed more improved crystallinity, smoother surface, and smaller grain size than that with 1 mol%Ni/1 mol%Ce. The dielectric constant and loss of Ni/Ce co-doped BST films were about 298 and 1.8%, respectively. In addition, tunability and figure of merit of co-doped BST films showed minimum values of approximately 9.3% and 5, respectively. With 1% Ni-doped BST thin films, results gave a tunability of 54.2% and a loss tangent of 1.8% while a figure of merit was 30. Correlation of the material properties with dielectric and tunable properties suggests the 1 mol%Ni-doped BST films are effective potential candidate for tunable device applications. [ABSTRACT FROM AUTHOR]