Comparative Study on Combined Addition of Gd-Ce and Gd-Y on the Mechanical Properties and Electrochemical Behavior of Mg-Zn-Mn-Ca Alloys.

This study presents a comparative analysis of the influence of Ce-Gd and Gd-Y additions on the microstructural evolution, mechanical properties, and electrochemical behavior of extruded Mg-3Zn-Mn-Ca alloy rods. Despite the frequent incorporation of Gd, Y, and Ce as alloying elements in magnesium alloys, the systematic examination of their combined effects on Mg-Zn alloys has been limited. Our findings reveal that both Gd-Ce and Gd-Y additions significantly enhance the mechanical properties of Mg-3Zn-Mn-Ca alloy, although through differing mechanisms. Specifically, the Mg-3Zn-1Mn-0.5Ca-1Gd-0.5Ce(ZMXE3101(GdCe)) alloy exhibited a yield strength of 304.5 MPa and an elongation of 15%, achieved through dynamic recrystallization and enhanced basal texture. The grain refinement and texture strengthening resulting from the coarse second-phase particles formed by Ce-Gd played a significant role in increasing the yield strength. In contrast, the Mg-3Zn-1Mn-0.5Ca-1Gd-0.5Y (ZMXE3101(GdY)) alloy demonstrated a yield strength of 305 MPa and an elongation of 20%. The finer grains and elongated unrecrystallized grains formed by Gd-Y contributed to the elevation in yield strength. While the ductility of this alloy was slightly lower than that of Mg-3Zn-Mn-Ca without rare earth additions, it still exhibited commendable overall mechanical properties. The electrochemical test results indicate that the addition of both Gd-Ce and Gd-Y enhances the corrosion current density of Mg-3Zn-Mn-Ca alloy, attributable to the generation of numerous rare earth phase particles that function as cathodes. Compared to the ZMXE3101(GdY) alloy, ZMXE3101(GdCe) exhibits a higher equilibrium potential and significantly lower corrosion current density. This is due to the formation of a protective film during the corrosion process by Gd-Ce.