Inhibitory effects of chlorhexidine-loaded calcium carbonate nanoparticles against dental implant infections.

This study aimed to design sustained released biodegradable calcium carbonate nanoparticles loaded with chlorhexidine (CHX-loaded NPs) and to investigate the early osteogenic differentiation and antimicrobial effects on the important bacteria involved in infections of dental implants. The microemulsion method was used to prepare the calcium carbonate nanoparticles loaded with chlorhexidine. The prepared nanoparticles were characterized using conventional methods. The release pattern determination and the biodegradation test were performed for the prepared nanoparticles. For the early osteogenic differentiation test of the prepared nanoparticles, alkaline phosphatase (ALP) activity was detected in human dental pulp stem cells (HDPSCs). The antimicrobial effects of the nanoparticles were evaluated against Escherichia coli, Streptococcus mutans, Enterococcus faecalis, Staphylococcus aureus, and Pseudomonas aeruginosa. The sizes of free calcium carbonate nanoparticles and CHX-loaded NPs were 105 ± 1.63 and 118 ± 1.47 nm and their zeta potentials were - 27 and - 36, respectively. A 50% degradation of nanoparticles was achieved after 100 days. These nanoparticles showed a two-stage sustained release pattern in vitro. Microscopic images revealed that the morphology of free calcium carbonate nanoparticles primarily took on a spherical calcite form, while CHX-loaded NPs predominantly exhibited a cauliflower-like vaterite polymorph. The nanoparticles increased the activity of ALP in cells in two weeks significantly (p < 0.05). Antimicrobial and antibiofilm results showed an efficient effect of the prepared nanoparticle against the studied bacteria. Calcium carbonate nanoparticles are an efficient multifunctional vector for chlorhexidine and can be used as a bioactive antibacterial agent against various oral microorganisms to prevent implant infections.
(© 2024. The Author(s).)