A comprehensive approach for the recycling of anode materials from spent lithium-ion batteries: Separation, lithium recovery, and graphite reutilization as environmental catalyst.

The effective recovery of valuables from anodes coming from spent lithium-ion batteries (LIBs) is of great importance to ensure resource supply and reduce the environmental burden for recycling. In this work, a simple and low energy consumption roasting method was proposed by employing low-temperature eutectic NaOH-KOH as reaction medium, in order to simultaneously separate graphite from Cu foils, extract lithium from it and set it up for reuse as environmental catalyst through one-step water washing process. Our results show that polyvinylidene difluoride (PVDF) was effectively deactivated due to dehydrofluorination/carbonization at a relatively low temperature and short time (150 °C, 20 min) when a mass ratio of 1:1 for eutectic NaOH-KOH to spent LIBs anodes was used, yielding 97.3 % of graphite detached. Moreover, a remarkable lithium extraction efficiency of 93.2 % was simultaneously obtained. Afterwards, the reusability of the recycled graphite was tested by employing it as a catalyst for the treatment of a contaminant organic dye (Rhodamine B) in the presence of NaClO. Our results show that a superior NaClO activation was obtained with the addition of recycled graphite, being this fact closely associated to the abundant active sites formed during the long-term charging/discharging cycles in the original battery. The alkaline-mediated roasting process presented in this work presents an energy-saving scheme to efficiently recover useful components from spent anodes, whereas the reusability example highlighted a useful option for repurposing the severely damaged graphite as an environmental catalyst rather than disposing it in landfills, turning waste into a valuable material.
Competing Interests: Declaration of competing interest The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
(Copyright © 2024 The Author(s). Published by Elsevier Ltd.. All rights reserved.)